| Item | Issue | Solution | Benefits |
| Machine parts | Corrosion (rust) on unprotected parts or zinc plated parts. Paint chipping and general deterioration over time. Hard to clean & maintain aesthetically | Coating of approx. 10 mm high phosphorous ENi | Provided corrosion resistance, wear resistance and ease of cleaning |
| Machine shafts | Excessive wear around seal area | New shafts made allowing for 50 mm deposit of ENi and harden to 65 RC | Wear at this area has been improved dramatically. Life of parts extended to the point where seals wear out first |
| Pivot pin | Previously nitrided and then hard chromed. Although wearing well, corrosion evident around seal areas | Samples machined to allow for 50 mm deposit of ENi then hardened to 65RC | Wear characteristics maintained. Corrosion no longer a problem. Life of parts extended. |
| Threaded drive screw (brass) | Parts running on plastic which was picking up brass particles from the screws creating excessive wear on the plastic running surface | 5-8 mm deposit of ENi on brass screw | Harder ENi coating eliminated "pick up". Also increased life of parts and provided corrosion resistance. |